PROGRAMMA DI RICERCA 2005

italiano - english
Unità di Ricerca
Programmi di ricerca simili:
Classificazione scientifico-disciplinare
Classificazione brevettuale
  • CHEMISTRY; METALLURGY
    • DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; MISCELLANEOUS COMPOSITIONS; MISCELLANEOUS APPLICATIONS OF MATERIALS
      • COATING COMPOSITIONS, e.g. PAINTS, VARNISHES, LACQUERS; FILLING-PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR (cosmetics A61K; processes for applying liquids or other fluent materials to surfaces, in general B05D; staining wood, B27K5/02; polymers in general C08F, C08G; organic dyes or closely-related compounds for producing dyes, mordants or lakes, per se, C09B; treatment of inorganic materials other than fibrous fillers used as pigments or fillers C09C; natural resins, French polish, drying-oils, driers, turpentine, per se, C09F; polishing compositions other than French polish, ski waxes C09G; preparation of glue or gelatine C09H; adhesives or use of materials as adhesives C09J; processes for the electrolytic or electrophoretic production of coatings C25D; textile-treating compositions D06; paper-making D21; conductors, insulators H01B)
Classificazione geografica
Bibliografia
1. A.D. Wilson, J.W. Nicholson, H.J. Prosser “Waterborne Coatings, Surface Coatings 3”, Elsevier Applied Science, London, 1990
2. E.H. Colstee “Approaches to protecting steel with waterborne coatings”, Protective Coatings Europe, July 1997;
3. J.C. Padget, “Polymers for Water-based coatings – a systematic overview”, J. Coat. Technol.; 66, 89-105 (1994)
4. Z.W. Wicks, F.N. Jones, S.P. Pappas, in: “Organic Coatings Science and Technology”, vol.1, Wiley (NY), 1992, pp.188-211
5. M. Dahm, H. Ehlert, F. Muller, H. Toepsch, H. Traubel, W. Wieczorrek, in: “Polyurethane Handbook“, G. Oertel, ed., Hanser (Munich), 1994, pp. 555-593
6. M. Dieterich, “Aqueous emulsions, dispersions and solutions of polyurethanes: synthesis and properties”, Progr. Org. Coat.; 9, 281-340 (1981)
7. J.W. Rosthauser, K. Natchkamp, “Waterborne polyurethanes”, in: “Advances in Urethane Science and Technology”, K.C. Frisch, D. Klempner, eds, vol.10, pp.121-162 (1987)
8. B.K. Kim, J.C Lee, “Waterborne polyurethanes and their properties”, J. Polym. Sci., Part A: Polym. Chem.; 34, 1095-1104 (1996)
9. S. Ramesh, K. Tharanikkarasu, G.N. Mahesh, G. Radhakrishnan, “Synthesis, physicochemical characterisation and applications of polyurethane ionomers: a review”, J. Macromol. Sci.; C: Reviews, 38, 481-510 (1998)
10. J.E.Yang, J.S. Kong, S.W. Park, D.J. Lee, H.D. Kim, “Preparation and properties of waterborne polyurethane-urea anionomers”, J. Appl. Polym. Sci.; 86, 2375-2383 (2002)
11. C.R. Hegedus, A.G. Gilicinski, R.J. Haney, “Film formation mechanism of two-component waterborne polyurethane coatings”, J. Coat. Technol.; 68, 51-51 (1996)
12. R.G. Coogan, “Post-crosslinking of water-borne urethanes”, Progr. Org. Coat.; 32, 51-63 (1997)
13. M. Melchiors, M. Sonntag, K, Kobusch, J. Eberhardt, “Recent developments in aqueous two-component polyurethane coatings“, Progr. Org.Coat.; 40, 99-109 (2000)
14. Z. W.Wicks, D. A. Wicks, J. W. Rosthauser, “Two package waterborne urethane systems”, Progr. Org. Coat.; 44, 161-183 (2002)
15. M. Delucchi, S. Turri, A. Barbucci, M. Bassi, S. Novelli, G. Cerisola, “Fluoropolyether coatings: relationships of electrochemical impedance spectroscopy measurements, barrier properties, and polymer structure”, J. Polym. Sci.; Part B: Polym. Phys., 40, 52-64 (2002)
16. R. Canteri, G. Speranza, M. Anderle, S. Turri, S. Radice, “TOF-SIMS and XPS surface characterisation of novel perfluoropolyether-urethane ionomers form aqueous dispersions”, Surf. Interface Anal.; 35, 318-326 (2003)
17. Z. Wang, D. Gao, J. Yang, Y. Chen, “Synthesis and characterisation of UV-curable waterborne polyurethane-acrylate ionomers for coatings”, J. Appl. Polym. Sci.; 73, 2869-2876 (1999)
18. F. Masson, C. Decker, T. Jaworek, R. Schwalm, “UV-radiation curing of waterbased urethane-acrylate coatings“, Progr. Org. Coat.; 39, 115-125 (2000)
18. F.Masson, C.Decker, Macromol.Mat.Eng. 288, 17-22 (2003);
20. S.P.Pappas (Ed.), Radiation Curing, Science And Technology, Plenum Press, New York, 1992, Chapter 1
21. Y.Okamoto et al. Adhesives, Sealants and Coatings for space and harsh environment Plenum Press, New York;
22. G.Hougham, K.Johns, P.E.Cassidy, T.Davidson Fluoropolymers: Synthesis And Properties, Plenum Publ., New York, 1999;
23. N.N.Chuvatkin, I.Y.Panteleeva in Modern Fluoropolymers J.Scheirs ed., Wiley Chichester, 1997 Chapter 9;
24. 11. M.Torstensson, B.Ranby, A.Hult Macromolecules 1990, 23, 126;
25. Y.Takezawa, S.Tanno, N.Taketani, S.Ohara, H.J.Asano Appl. Poly. Sci. 42, 1991, 3195;
26. R.Bongiovanni, G.Malucelli et al. Macromol.Chem.Phys. 199, 1998, 1099;
27. B.Ameduri, R.Bongiovanni, G.Malucelli, N.Pollicino, A.Priola, J. Polym. Sci. Polym. Chem. 37, 1999, 77;
28. R.Bongiovanni, G.Beamson, A.Mamo, A.Priola, A.Recca, C.Tonelli, Polymer 41, 2000, 409;
29. B.Ameduri, R.Bongiovanni et al. J.Polym.Sci. Part A: Polym Chem, 39, 2001, 4227;
30. R.Bongiovanni, F.Montefusco, A.Priola, N.Macchioni, S.Lazzeri, L.Sozzi, B.Ameduri Progr. Org. Coatings 1223, 2002, 1;
31. 9. A.J. Reuvers, “Control of Rheology of waterborne paints using associative thickeners”, Proc. Int. Conf. Org. Coat.: Waterborne, High Solids, Powder Coat., Institute of Materials Science, New Paltz, N.Y., 24th Edition, 337-356 (1998);
32. R.H. Fernando, L.L. Xing, J.E. Glass, Progress in Organic Coatings, 40, 35-38 (2000);
33. K. Doren, W. Freitag and D. Stoye (Eds) “Water-Borne Coatings: The Environmentally-friendly Alternative” Hanser Publishers, Munich 1994;
34. M.Alexandre, P.Dubois Materials Sci, Eng. 15, 2000, 1;
35. P. Giannelis Adv.Materials 8,1996, 29
36. A. Usuki, M.Kawasumi, Y.Kojima et al. J.Mater. Res. 8, 1993, 1174
37. D.Shah, P.MAiti, D.D.Jang, E.P.Giannelis Adv.Materials 16, 2004, 1173
38. B.S. Shemer, J.F.Morizur, M.Alirol, A.Domenech, V.Hulin, L.J.Mathias JAPS 93, 1252, 2004
39. C.Decker, K.ZAhouily et al. J.Mater. Sci. 37, 4831, 2002
40. F.Uhl, B.R. Hinderliter et al. Poym Prepr ACS 44, 247, 2003
41. G.C. Xu, A.Y. Li et al. JAPS 90, 837, 2003
42. S. Benfarhi, C. Decker et al. Eur. Polym. J. 40, 493, 2004
43. C. Decker al in Nano and hybrid coatings PRA conference MAnchester 2005 Proceedings paper 1
44. H.J. Glasel et al Macromol. Chem. Phys. 201, 2765, 2000
45. B.J.Falk J.V. Crivello Chem.Mater. 16, 5033, 2004
46. M. Osterhold, European Coatings Journal, 4 18-33 (2000)
47. Baure D., Martin J., "Service life prediction of organic coatings", Oxford University Press, London, 1999;
48. Watts J. F, J. Adhesion, 31, 73-85, (1989)
49. G. W. Walter, Corros. Sci. 26, 703 (1986)
50. F. Mansfeld, J. Appl. Electrochem. 25, 187 (1995)
51. Stratmann, M., Leng, A., Fürbeth, W., Streckel, H., Gehmecker, H., Groβe-Brinkhaus, K.-H., Progress Organic Coatings, 27, 261 (1996).
Parole Chiave
RIVESTIMENTI ORGANICI; IMPATTO AMBIENTALE; RETICOLAZIONE UV; VERNICI ALL'ACQUA; RIVESTIMENTI NANOCOMPOSITI; PROTEZIONE DALLA CORROSIONE; PROVE ELETTROCHIMICHE

Nuovi rivestimenti nanocompositi ottenuti per fotoreticolazione da dispersioni acquose

Università degli Studi di Trento
Abstract
La ricerca nazionale ed internazionale già da alcuni anni si sta muovendo nella direzione di uno sviluppo di prodotti vernicianti protettivi a ridotto impatto ambientale. Fra le sostanze che si cercano di ridurre, per avere prodotti più ecologici, ci sono i pigmenti anticorrosivi tossici e i solventi organici.
Sulla base delle conoscenze attuali, le vernici a base acqua e quelle fotoreticolabili rappresentano le soluzioni più promettenti per evitare emissioni nocive e la combinazione dei due sistemi, vernici fotoreticolabili a base acqua, può fornire anche interessanti miglioramenti tecnologici e applicativi.
Inoltre l'aggiunta di nanoparticelle o nanoargille lamellari, come ad esempio nanoossidi, nanosilici e fillosilicati stratificati può migliorare sensibilmente le proprietà protettive, quelle meccaniche e la durabilità nel tempo.
Un prodotto verniciante a base acqua e fotoreticolabile con l'aggiunta di nanopigmenti rappresenta una novità nell'ambito dei prodotti vernicianti ecologici.
Ogni volta che viene studiato un nuovo prodotto verniciante è necessario che siano attentamente monitorate le proprietà tecnologiche di interesse, in particolare le capacità protettive (proprietà di barriera ad ioni, acqua e altre specie aggressive, assenza di difetti, ecc.) e la capacità di aderire al substrato.
Vista la molteplicità delle possibili applicazioni, è importante verificare che le proprietà protettive o di barriera e l'adesione al substrato >>>

Coordinatore Scientifico del Programma di Ricerca
Flavio DEFLORIAN Università degli Studi di TRENTO
Obiettivo del Programma di Ricerca
In questo progetto di ricerca l'attività delle diverse U.O. partecipanti sarà rivolta alla progettazione, preparazione e caratterizzazione di nuovi sistemi polimerici per prodotti vernicianti all'acqua, fotoreticolati e nanostrutturati e all'analisi della loro durabilità in ambienti aggressivi per verificarne la reale possibilità di utilizzo industriale.
L'attività sopracitata prevede uno sviluppo temporale di 24 mesi attraverso il raggiungimento di risultati correlabili a fasi intermedie che possono essere focalizzate come segue:
-­sintesi e caratterizzazione molecolare di sistemi polimerici nanocompositi a base acquosa con funzioni fotoreticolabili;
-formulazioni per UV-curing a base acqua;
-­preparazione di rivestimenti nanocompositi con tecnologie pulite (UV-curing) a base acqua.
-­caratterizzazione dei rivestimenti di nuova formulazione applicate su appositi substrati attraverso lo studio microstrutturale, chimico-fisico, dell'adesione substrato-rivestimento e lo studio della resistenza al degrado ambientale fisico-meccanico.
Dettaglio maggiore è riportato nei programmi di ricerca delle singole unità.

Durata
24 mesi
Base di partenza scientifica nazionale o internazionale
La ricerca nazionale ed internazionale già da alcuni anni si sta muovendo nella direzione di uno sviluppo di prodotti vernicianti protettivi a ridotto impatto ambientale. Fra le sostanze che si cercano di ridurre, per avere prodotti più ecologici, ci sono i pigmenti anticorrosivi tossici e i solventi organici. Le vernici a base acqua sono una delle possibilità più interessanti assieme a quelle ad alto solido (1-2).
Uno dei limiti più importanti di questi prodotti sono le condizioni di applicazione che spesso presentano una notevole criticità (difficoltà di stesura per problemi reologici, controllo di temperatura ed umidità relativa per avere un curing adeguato, ecc.)
E' quindi abbastanza frequente che il grado protettivo di questi prodotti vernicianti a ridotto impatto ambientale sia non soddisfacente, e questo limita fortemente il loro reale utilizzo industriale.
E' quindi chiaro che ogni volta che viene studiato un nuovo prodotto verniciante è necessario che siano attentamente monitorate le proprietà tecnologiche di interesse, in particolare le capacità protettive (proprietà di barriera ad ioni, acqua e altre specie aggressive, assenza di difetti, ecc.) e la capacità di aderire al substrato, in genere di natura metallica.
Inoltre tali proprietà non devono soltanto essere valutate per il prodotto così come è stato depositato, ma è necessario permangano in esercizio. E' cioè importante verificare che le proprietà protettive o di barriera e >>>